POLYSTONE® G black B 100
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Röchling Engineering Plastics SE & Co. KG |
| Trademark: | POLYSTONE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nLmbN0_POLYSTONE-G-black-B-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Product characteristics
Typical field of application
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.22 | g/10 min | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.010 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 10 | % | |
| Break | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | > 16 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature | |||
| -- 1 | -50.0 to 80.0 | °C | |
| -- 2 | < 100 | °C | |
| Melting Temperature | 135 | °C | ISO 11357-3 |
| CLTE - Flow | 1.5E-4 to 2.3E-4 | cm/cm/°C | DIN 53752 |
| Specific Heat | 1900 | J/kg/°C | DIN 52612 |
| Thermal Conductivity | 0.40 | W/m/K | DIN 52612 |
| Heat Deflection Temperature - Vicat B | 67 | °C | ISO 306 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance | L4 degree | IEC 60093 | |
| Material Designation | PE-EACH-50T003 | ISO 1872 | |
| MRS Classification | PE100 | ISO TR 9080 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 45 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 2.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 4.0E-4 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | HB | ||
| 6.00 mm | HB |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC EVA VC710 | Lotte Chemical Corporation | EVA | SEETEC EVA |
| NYLAFORCE® B 50 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 6 | NYLAFORCE® |
| Hyosung Polyketone M330A | Hyosung Corporation | PK-Aliphatic | Hyosung Polyketone |
| REV Materials 8006-001 | REV Materials | PP, Unspecified | REV Materials |
| VisiJet® FTX Clear | 3D Systems | Unspecified | VisiJet® |