AFFINITY™ PL 1880G
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AFFINITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nLCFEB_AFFINITY-PL-1880G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
AFFINITY* PL 1880G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is an ethylene alpha-olefin resin designed for use in a variety of demanding packaging applications, including high-speed, form-fill-seal packaging. This resin offers excellent ultimate hot tack strength and low temperature seal initiation, even through contamination in the package.
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.902 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Energy (51 µm) | 8.81 | J | Internal method |
| Film Puncture Force (51 µm) | 92.5 | N | Internal method |
| Film Puncture Resistance (51 µm) | 22.3 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 91.7 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 92.4 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 7.24 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 6.89 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 58.6 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 44.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 620 | % | ASTM D882 |
| TD : Fracture, 51 µm | 630 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | > 830 | g | ASTM D1709B |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 51 µm | 550 | g | ASTM D1922 |
| TD : 51 µm | 720 | g | ASTM D1922 |
| Seal Initiation Temperature 2(51 µm) | 85.0 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 86.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 99.0 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.8 µm) | 141 | ASTM D2457 | |
| Clarity (50.8 µm) | 83.0 | ASTM D1746 | |
| Haze (50.8 µm) | 1.1 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 209 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：SFDM 模具间隙：70 密尔 (1.8 mm) 熔体温度：408°F (209°C) 输出：模具周长的 6 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：50 rpm |
| Note Message | |
|---|---|
| 1 . | Modified rectangular test piece. |
| 2 . | Achieve a temperature of 2 psig (8.8 N/25.4mm) heat seal strength. Heat seal strength, Topwave HT tester 0.5 S holding pressure, 40 psi pressure, pulling speed 10 inches/min (250 mm/s). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5132-84 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TYMAX® GT4402 | Westlake Chemical Corporation | LLDPE | TYMAX® |
| Complet® LGF40-PP | PlastiComp, Inc. | PP Homopolymer | Complet® |
| LNP™ THERMOTUF™ WF006N compound | SABIC Innovative Plastics Asia Pacific | PBT | LNP™ THERMOTUF™ |
| ESTOPLAST XU 6215BB11 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |