Lutene® FB0300
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lutene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nL7zcH_Lutene-FB0300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LUTENE FB0300 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of heavy duty sacks and pallet shrink films. LUTENE FB0300 have the excellent mechanical properties and high stress cracking resistance make suitable for heavy duty bags and particularity bottom sealed bags. (LUTENE FB0300 contains no slip agent.) Applications: Packing of heavy products, Shrink hoods, Pallet shrink covers, all types of industrial packing |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | > 500 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Resistance | ASTM D1922 | ||
| MD | 36.3 | MPa | ASTM D1922 |
| TD | 37.3 | MPa | ASTM D1922 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Nitrogen Permeability | 3500 | cm³/m²/24 hr | Internal method |
| Film Thickness - Tested | 50 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 23.5 | MPa | ASTM D882 |
| TD : Fracture | 22.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 550 | % | ASTM D882 |
| TD : Fracture | 650 | % | ASTM D882 |
| Dart Drop Impact | 300 | g | ASTM D1709 |
| Oxygen Permeability | 2000 | cm³/m²/24 hr | Internal method |
| Water Vapor Transmission | 10 | g/m²/24 hr | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Melting Temperature | 110 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 95 | ASTM D2457 | |
| Haze | 17 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 220 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 1.5 to 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KEG-2000-20A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Sylvin 2910-85 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| WELLAMID Nylon 6000/58 CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| SABIC® EPDM 626 | Saudi Basic Industries Corporation (SABIC) | EPDM | SABIC® EPDM |
| AURUM® JCN6230 | Mitsui Chemicals, Inc. | PI, TP | AURUM® |