Reny® 1507
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nIWXhN_Reny-1507.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® 1507 is a Polyarylamide (PARA) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® 1507 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 169 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2 |
| Flexural Modulus | 12000 | MPa | ISO 178 |
| Flexural Stress | 288 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.8 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 52 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 222 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 325 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 120 to 145 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ LC-20NCF/000 V3 Natural | PolyOne Corporation | LCP | Stat-Tech™ |
| Elastollan® C 75 A HPM | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| LUVOCOM® 1/SCF/30/TF/15 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Hostacom TRC 333N D72645 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sarlink® TPV X4145B-W1 BLACK (PRELIMINARY DATA) | Teknor Apex Company | TPV | Sarlink® TPV |