VALOX™ SHF4330 resin
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nHx1wg_VALOX-SHF4330-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
15% GF reinforced PBT/ASA, High Flow version |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 40.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.20 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 160 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 5300 | MPa | ASTM D638 |
| -- | 5400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 85.0 | MPa | ASTM D638 |
| Yield | 85.0 | MPa | ISO 527-2/5 |
| Break 4 | 85.0 | MPa | ASTM D638 |
| Break | 85.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Break 6 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 7 | 4800 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Flexural Strain at Break 8 | 3.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 15 | % | ASTM D229 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Notched Izod Impact Strength 9 | ISO 180/1A | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Unnotched Izod Impact Strength 10 | ISO 180/1U | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 28 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 11 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 204 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 152 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 215 | °C | ISO 306/A50 |
| -- | 157 | °C | ISO 306/B50 |
| -- | 159 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (280°C, 1500 sec^-1) | 55.0 | Pa·s | ISO 11443 |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® Pouch PE2718 | Tekni-Films, a div of Tekni-Plex | Film, Polyester/PE/Al Foil/LLDPE | TEKNIFLEX® Pouch |
| BP ABS 3333 R BLK | Buckeye Polymers, Inc. | ABS | BP |
| Hostalen ACP 5531 B | LyondellBasell Industries | HDPE | Hostalen |
| Laprene® 830000971 | SO.F.TER. SPA | SEBS | Laprene® |
| MARPOL® LL4M 850-G | Marco Polo International, Inc. | LLDPE | MARPOL® |