MAJORIS CETAL GN032
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nHYMXk_MAJORIS-CETAL-GN032.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CETAL GN032 is a polyoxymethylen (POM), intended for injection moulding grade with high flow, anti-static modified. APPLICATIONS The product is available in both natural but other colours can be provided on request. CETAL GN032 has been developed especially for the automotive applications and electrical components. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 27 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.8 - 2.0 | % | |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.70 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1 |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 8.0 | % | ISO 527-2/1A/50 |
| Fracture | 17 | % | ISO 527-2/1A/50 |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.5 | kJ/m² | ISO 179 |
| 23°C | 6.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Injection Pressure | 60.0 - 200 | MPa | |
| Back Pressure | 0.00 - 2.00 | MPa |
| Injection instructions |
|---|
| Holding pressure: egal injection pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GS25-66 22LH-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| YUZEX® 7210 | SK Global Chemical | HDPE | YUZEX® |
| 3M™ Dyneon™ PTFE Compound TF 8615 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Kuraray Poval® PVA 505 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| LEXAN™ HP2EU resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |