HIPTEN® 22020
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | HIP-PetroHemija |
| Trademark: | HIPTEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nHCiRt_HIPTEN-22020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIPTEN® 22020 is low density polyethylene resin developed for film extrusion. This grade has good mechanical and optical properties and good draw down characteristics. Film produced from this grade has good appearance and heat sealability, good moisture barrier and adhesion properties. Applications: Production of laminated food-packaging materials. HIPTEN® 22020 has Health Certificate issued by Institute for Health Protection of Serbia. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 46 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 9.00 | MPa | ISO 527-2 |
| Fracture | 12.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 600 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| TD : Yield, 40 µm, blown film | 12.0 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 20.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 19.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 650 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 750 | % | ISO 527-3 |
| Dart Drop Impact (40 µm) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 40.0 µm | 135.1 | kN/m | ASTM D1922 |
| TD : 40.0 µm | 173.7 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 200 | °C |
| Extrusion instructions |
|---|
| Blow-up ratio: 2:1 to 3:1 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP792P | Southern Polymer, Inc. | HDPE | PRIMALENE |
| Quantum Composites QC-8700 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Spartech Polycom X03747 | Spartech Polycom | PP, Unspecified | Spartech |
| LNP™ LUBRICOMP™ DL003EU compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Pinnacle PP 5120H | Pinnacle Polymers | PP Random Copolymer | Pinnacle PP |