Ultrason® E KR 4113
| Category: | PESU , Polyethersulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nH4ATR_Ultrason-E-KR-4113.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PES with 30 % filler. The filler system, a mixture of carbon fibres, graphite and PTFE powder, considerably improves Ultrason tribological properties. In addition, this product has a very small expansion coefficient and low tendency to swell in hot oils. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.46 | % | |
| Flow | 0.31 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.5 | % | |
| Equilibrium, 23°C, 50% RH | 0.50 | % | |
| Viscosity Number 1 | 56.0 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 180 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 6.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 24 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 5.5 | kJ/m² | |
| 23°C | 6.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 223 | °C | ISO 75-2/A |
| Glass Transition Temperature 2 | 225 | °C | ISO 11357-2 |
| CLTE - Flow | |||
| 23 to 80°C | 1.1E-5 | cm/cm/°C | ISO 11359-2 |
| 180°C | 1.3E-5 | cm/cm/°C | DIN 53752 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+3 | ohms | IEC 60093 |
| Volume Resistivity | 9.0E+5 | ohms·cm | IEC 60093 |
| Electric Strength | 8.0 | kV/mm | IEC 60243-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 350 | °C | |
| Middle Temperature | 360 | °C | |
| Front Temperature | 370 | °C | |
| Nozzle Temperature | 370 | °C | |
| Processing (Melt) Temp | 350 to 390 | °C | |
| Mold Temperature | 150 to 190 | °C | |
| Screw Speed | < 300 | mm/sec |
| Note Message | |
|---|---|
| 1 . | in 0,01 g/ml Phenol/1,2, ortho-Dichlorbenzol, 1:1 |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1985NT | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sylvin 2944-91 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Topolymer® 9210-503 | Dongguan Top Polymer Enterprise | TPV | Topolymer® |
| Karina BROWN COLOR CONCENTRATE 36/234-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| apilon 52® D1 58 | API SpA | TPU-Polyester | apilon 52® |