| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nGouMx_Propafilm-OS80.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Speed Overwraping Film with Shrink Tightening Properties Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with heat sealable polyolefinic copolymers. OS80/100 are suitable for high speed overwrapping applications where exceptional pack appearance and wrap tightness are required. Particularly suitable for the magnectic media, confectionery and tea industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 80°C, 1 min | 3.7 | % | |
| Flow : 120°C, 1 min | 7.0 | % | |
| Across Flow : 80°C, 1 min | 3.5 | % | |
| Across Flow : 120°C, 1 min | 11 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.25 | ||
| vs. Itself - Static, Outside/Outside | 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus 1 | ASTM D882 | ||
| 1% Secant, MD | 3000 | MPa | |
| 1% Secant, TD | 3600 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield | 170 | MPa | |
| TD : Yield | 210 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break | 120 | % | |
| TD : Break | 80 | % | |
| Seal Strength 4 | 0.19 | N/mm | Internal Method |
| Seal Initiation Temperature 5 | 116 to 141 | °C | Internal Method |
| Oxygen Permeability (23°C, 0% RH) | 38 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate | ASTM F1770 | ||
| 23°C, 85% RH | 0.93 | g/m²/24 hr | |
| 38°C, 90% RH | 6.0 | g/m²/24 hr | |
| Film Gauge | 80.0 | Internal Method | |
| Yield | 54.9 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°) | 140 | ASTM D2457 | |
| Haze 6 | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 10%/min |
| 2 . | 50%/min |
| 3 . | 50%/min |
| 4 . | 225°F; 1sec; 15lb/in² |
| 5 . | 2secs; 15lb/in² |
| 6 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1002 TFE 10 | RTP Company | PBT | RTP |
| DOW™ Butene 1211P | The Dow Chemical Company | LLDPE | DOW™ Butene |
| Kotex K-40 | Kotec Corporation | PC | Kotex |
| LNP™ THERMOCOMP™ UF0067W compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| Sylvin 8980-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |