MAJORIS AN060
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nGWXZA_MAJORIS-AN060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AN060 is a polypropylene copolymer compound, for extrusion applications. APPLICATIONS AN060 is recommended for the extrusion of profiles (Automotive parts, building, electrical, furniture and construction profiles or pipes). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 35.0 | MPa | |
| Break | 39.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | 500 | % | |
| Flexural Modulus 1 | 1500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | 70 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 94.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 155 | °C | ISO 306/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 190 to 230 | °C | |
| Cylinder Zone 3 Temp. | 190 to 230 | °C | |
| Cylinder Zone 5 Temp. | 190 to 230 | °C | |
| Melt Temperature | 200 to 230 | °C | |
| Head Temperature | 200 to 230 | °C | |
| Die Temperature | 200 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Ofluorine PVDF 904 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| Sup-tech S703 | Shanghai Suptech Engineering Plastics Co. Ltd. | ABS | Sup-tech |
| Novalloy-B B27B6 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| Bergamid™ Bergamid™ A65 GK15 natur SOx | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Aropol™ RTM 80501 | Ashland Performance Materials | Polyester, TS | Aropol™ |