NEMCON E PET 30131
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | NEMCON E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nGINYg_NEMCON-E-PET-30131.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PET - Fiber Grade with ESD Range Conductivity with improved processability. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2550 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 52.0 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.6 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 3090 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 20 | J/m | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.1E+4 | ohms | ASTM D257 |
| Additional Information |
|---|
| The value listed as Surface Resistivity ASTM D257, was tested in accordance with Ovation Polymers internal testing methods. |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200-90A | RTP Company | TPU-Polyester | RTP |
| Promyde® B30 P2 G30 U0 | NUREL, S.A. | Nylon 6 | Promyde® |
| WPP PP PPHFGC-3 | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Clariant Nylon 6/6 PA-113G43 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Durez® 118 (Compression) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |