BESTNYL SI00VI02BEHX
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nGGL47_BESTNYL-SI00VI02BEHX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 black extrusion, lubricated and V-0 grade free halogen with heat stabilized |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ISO 62 |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Test | OK | IEC 60695-2-13 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 79 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 68 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 180 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Electric Strength | 18 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 225 to 240 | °C | |
| Mold Temperature | 4.00 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Metabolix I6001 | Metabolix | PHA | Metabolix |
| Starex LX-0970 LS | SAMSUNG SDI CO., LTD. | ABS | Starex |
| EPO-TEK® 310M Black | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Hostacom PPW 1752HL21 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 9077-75 Yellow 4181 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |