NORYL™ FN215X resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nFHpBN_NORYL-FN215X-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Structural foam resin. 170F (77C) HDT. Improved reliability and productivity. All values at 20% weight reduction. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 0.878 | g/cm³ | ASTM D792 |
| -- | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (6.40 mm) | 0.60 - 0.80 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.070 | % | ASTM D570 |
| Equilibrium, 23°C | 0.17 | % | ASTM D570 |
| Outdoor Suitability | f1 | UL 746C | |
| Foam - Physical 2 | 20 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Mechanical 3 | 20 | % | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Impact 4 | 20 | % | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Thermal 5 | 20 | % | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Flame Class Minimum Density | 850 | kg/m³ | Internal method |
| Radiant Panel Listing (UL) | YES |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 6.35 mm) | 29.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 6.35 mm) | 12 | % | ASTM D638 |
| Flexural Modulus (6.40 mm) | 1900 | MPa | ASTM D790 |
| Flexural Strength (Yield, 6.40 mm) | 61.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 6.40 mm) | 200 | J/m | ASTM D4812 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 3.28 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 11.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 88.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 76.7 | °C | ASTM D648 |
| RTI Elec | 85.0 | °C | UL 746 |
| RTI Imp | 85.0 | °C | UL 746 |
| RTI | 85.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+17 | ohms | ASTM D257 |
| Dielectric Strength (1.60 mm, in Oil) | 12 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 4.4E-3 | ASTM D150 | |
| Arc Resistance 6 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | V-1 | UL 94 | |
| 5.99 mm | V-0 | UL 94 | |
| 3.91 mm | 5VA | UL 94 |
| Additional Information |
|---|
| Structural Foam Molding - Blowing Agent, Physical System: Nitrogen GasStructural Foam Molding - Concentration Range (Blowing Agent): 1 - 3 %Structural Foam Molding - Drying Temperature (Resin): 71 - 82 °CStructural Foam Molding - Drying Time (Resin): 2 - 4 hrsStructural Foam Molding - Drying Time (Resin, Cumulative): 8 hrsStructural Foam Molding - Front Temperature: 271 - 304 °CStructural Foam Molding - Melt Temperature: 271 - 310 °CStructural Foam Molding - Middle Temperature: 271 - 304 °CStructural Foam Molding - Mold Temperature: 27 - 54 °CStructural Foam Molding - Nozzle Temperature: 271 - 304 °CStructural Foam Molding - Rear Temperature: 232 - 260 °CStructural Foam Molding - Recommended Concentration (Blowing Agent): 2 % |
| Note Message | |
|---|---|
| 1 . | Foam molded |
| 2 . | 6.4 mm wt reduction |
| 3 . | 6.4 mm wt reduction |
| 4 . | 6.4 mm wt reduction |
| 5 . | 6.4 mm wt reduction |
| 6 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom POM-C 5M-RDT | Witcom Engineering Plastics B.V. | Acetal (POM) Copolymer | Witcom POM-C |
| Appeel® 20D745 | DuPont Packaging & Industrial Polymers | AEM+TPC-ET | Appeel® |
| Kepital® FL2020 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Karina GRAY COLOR CONCENTRATE 18/212-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| RTP 699 X 123035 B Z | RTP Company | ABS | RTP |