Ipethene® 320
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Ipethene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nESCm7_Ipethene-320.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IPETHENE® 320 is a low density polyethylene extrusion grade, produced by high pressure autoclave technology. This grade is particularly suitable for the production of blown & cast transparent thin films. It has excellent draw-down, good optical and processing properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 24.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 21.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 500 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 750 | % | ISO 527-3 |
| Dart Drop Impact 1(50 µm, Blown Film) | 170 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 50 µm, blown film | 0.046 | N | ISO 6383-2 |
| TD : 50 µm, blown film | 0.025 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 93.0 | °C | ISO 306 |
| Melting Temperature 2 | 109 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 71 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 5.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties: Measured on 50 µm blown film, Blow-up ratio 2.5:1, output 10 kg/h, melt temperature ~170 °C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 155 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | By DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205.3 TFE 5 | RTP Company | Nylon 66 | RTP |
| TOTAL Polyethylene Lotrène® Q1018 H | TOTAL Refining & Chemicals | LLDPE | TOTAL Polyethylene |
| Capilene® W 77 AV | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| Iupilon® EHG2010R | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LUVOCOM® 50-8276 | Lehmann & Voss & Co. | PC | LUVOCOM® |