SCHULAMID® 6 MKF 4015
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nE55bH_SCHULAMID-6-MKF-4015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% glass fiber and mineral reinforced Polyamide 6 with high tensile strain at break and high dimension stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.45 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (Saturation, 23°C) | 1.9 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 205 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7000 | 4500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 110 | 70.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | 3.0 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 8.0 | kJ/m² | |
| 23°C | 8.0 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 60 | kJ/m² | |
| 23°C | 50 | 75 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 180 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 215 | -- | °C | ISO 306/A50 |
| -- | 210 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | -- | < 100 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | -- | HB | ||
| 3.00 mm | -- | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | -- | 650 | °C | |
| 3.00 mm | -- | 650 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOLEN R030 BM | SIBUR, LLC | PP Random Copolymer | TOLEN |
| Veromor® Purge -XT | PlastxWorld Inc. | Proprietary | Veromor® Purge |
| Elastron® D D100.A50.N | Elastron USA, Inc. | SBS | Elastron® D |
| ELASTOSIL® P 7600 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® P |
| Kynar® 761A | Arkema | PVDF | Kynar® |