LNP™ THERMOCOMP™ UF006S compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nCpu0G_LNP-THERMOCOMP-UF006S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* UF006S is a compound based on Polyphthalamide resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound UF-1006 HS Product reorder name: UF006S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % | |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 13600 | MPa | ASTM D638 |
| Tensile Strength (Break) | 197 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.4 | % | ASTM D638 |
| Flexural Modulus | 10200 | MPa | ASTM D790 |
| Flexural Strength | 276 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.48 | ||
| vs. Itself - Static | 0.43 | ||
| Wear Factor - Washer | 50.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 730 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 258 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 8.3E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.2E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 149 to 171 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3714 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Milastomer™ M4800NS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| Globalene® PT511 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| Hanwha Total PP HTH52 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| HIPLEX® TR 144 | HIP-PetroHemija | HDPE | HIPLEX® |