Sinkral® B 4 Milano
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Sinkral® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nCGgQZ_SinkralB4Milano.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
B 4 Milano is an extrusion grade specially suitable in aesthetics applications. It combines thermal characteristics and rheological properties which allow the extrusion of sheets also of large size with an excellent surface finishing (very low gels content). Designation: Thermoplastic ISO 2580-ABS 1,EGN,105-04-16-20 Applications Special grade for the realization of aesthetics goods that need typical ABS characteristics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.60 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 45.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 45 | % | ASTM D638 |
| Flexural Modulus 3 | 1850 | MPa | ASTM D790 |
| Flexural Strength 4 | 68.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | DIN 53453 |
| Charpy Unnotched Impact Strength | DIN 53453 | ||
| -40°C | No Break | DIN 53453 | |
| 23°C | No Break | DIN 53453 | |
| Notched Izod Impact | |||
| -40°C, 3.20 mm | 100 | J/m | ISO 180/4A |
| -20°C, 3.20 mm | 130 | J/m | ISO 180/4A |
| 0°C, 3.20 mm | 170 | J/m | ISO 180/4A |
| 23°C, 3.20 mm | 220 | J/m | ISO 180/4A |
| -40°C 5 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 6 | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 104 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 109 | °C | ISO 306/A120 |
| -- | 104 | °C | ISO 306/B120 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 kHz) | 3.10 | IEC 60250 | |
| Dissipation Factor (1 kHz) | 0.015 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (3.0 mm) | 650 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Designation | Thermoplastic ISO 2580-ABS 1,EGN,105-04-16-20 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Melt Temperature | 190 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 4 mm |
| 6 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toraycon® 5107G | Toray Resin Company | PBT | Toraycon® |
| TRIPET® 2500G40 | Samyang Corporation | PET | TRIPET® |
| ADDINYL A2 V30 | ADDIPLAST | Nylon 66 | ADDINYL |
| Nycal™ 2050R10 | Technical Polymers, LLC | Nylon 612 | Nycal™ |
| POLYfill PPH K8030 | Polykemi AB | PP Homopolymer | POLYfill |