DynaChar™ 3522
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Polymer Dynamix |
| Trademark: | DynaChar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nCDpep_DynaChar-3522.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flame Retardant TPO Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 30 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 138 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 11.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | > 500 | % | ASTM D412 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant | 2.40 | ASTM D1531 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 to 76.7 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 191 to 202 | °C | |
| Front Temperature | 199 to 210 | °C | |
| Nozzle Temperature | 199 to 210 | °C | |
| Processing (Melt) Temp | 199 to 210 | °C | |
| Mold Temperature | 10.0 to 37.8 | °C | |
| Injection Pressure | 68.9 to 138 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Clamp Tonnage | 5.5 to 8.3 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2000 Compression Molded Shape | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| TAROPRENE® 2 A80 E1G | Taro Plast S.p.A. | TPV | TAROPRENE® |
| Next PMMA AX-01D.GY. | Next Polymers Ltd. | Acrylic (PMMA) | Next PMMA |
| GLAMIDE® T-779 | TOYOBO America, Inc. | Nylon 6 | GLAMIDE® |
| Kemcor LD 1333 | Qenos Pty Ltd | MDPE | Kemcor |