DENKA Transparent Polymer TX-100S
| Category: | MMS , Methyl Methacrylate Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA Transparent Polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nBypmK_DENKA-Transparent-Polymer-TX-100S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DENKA Transparent Polymer TX-100S is a Methyl Methacrylate Styrene (MMS) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.8 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.40 | % | Internal Method |
| Water Absorption (Equilibrium) | 0.12 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 67.0 | MPa | ISO 527-2/5 |
| Nominal Tensile Strain at Break | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3400 | MPa | ISO 178 |
| Flexural Stress 2 | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 79.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 100 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 3 | 1.540 | ASTM D542 | |
| Transmittance (2000 µm) | 92.0 | % | ISO 13468-1 |
| Haze (2000 µm) | 0.20 | % | ISO 14782 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 240 | °C | |
| Middle Temperature | 190 to 240 | °C | |
| Front Temperature | 190 to 240 | °C | |
| Nozzle Temperature | 220 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | NA*D ray |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BCC Resins BC 8163 | BCC Products Inc. | PUR, Unspecified | BCC Resins |
| ICORENE® N4435 | ICO Polymers EMEA, A Division of A. Schulman | PP Homopolymer | ICORENE® |
| Petrotene® PP A3 G30 DOR0078 PH328 MSP | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| FUDOWPREMIX® FP100F typeB | Fudow Co., Ltd. | Polyester, TS | FUDOWPREMIX® |
| Edistir® N 3840 | Versalis S.p.A. | PS (GPPS) | Edistir® |