EPO-TEK® EK1000-MP
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nBW3Q3_EPO-TEK-EK1000-MP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A single component, silver-filled adhesive that exhibits exceptional thermal and electrical conductivity along with a shiny silver appearance making it ideal for the demanding requirements of high power LED die attach applications. Designed specifically to meet the requirements pertaining to the MIL-STD883/Test Method 5011 for military hybrids. Other benefits include low viscosity and high thixotropy making it suitable for a wide range of application techniques. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Ion Type | |||
| Cl- | < 200 | ppm | |
| K+ | < 50 | ppm | |
| Na+ | < 50 | ppm | |
| NH4+ | 5 | ppm | |
| Particle Size | < 45.0 | µm |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Dry Time | < 1.0 | day |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 357 | °C | |
| Die Shear Strength | |||
| >10 kg : 23°C 1 | 23.4 | MPa | |
| >5 kg : 23°C 2 | 11.7 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus | 1.89 | GPa | |
| Thixotropic Index | 3.60 | ||
| Weight Loss on Heating | |||
| 200°C | 0.19 | % | |
| 250°C | 0.94 | % | |
| 300°C | 1.7 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 3 | > 80.0 | °C | |
| CLTE - Flow | |||
| -- 4 | 3.8E-5 | cm/cm/°C | |
| -- 5 | 9.4E-5 | cm/cm/°C | |
| Thermal Conductivity | |||
| -- 6 | 13 | W/m/K | |
| -- 7 | 26 | W/m/K |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life (-40°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | Silver | ||
| Density | 3.33 | g/cm³ | |
| Viscosity 8(23°C) | 1.8 to 3.6 | Pa·s | |
| Curing Time (200°C) | 1.0 | hr | |
| Pot Life | 20000 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 66 | ||
| Lap Shear Strength (23°C) | 6.96 | MPa | |
| Volume Resistivity | < 9.0E-5 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Initial |
| 2 . | After 1000 hrs 85°C/85%RH |
| 3 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 4 . | Below Tg |
| 5 . | Above Tg |
| 6 . | 150°C/1 Hour Cure |
| 7 . | 150°C/1 Hour+200°C/1 Hour Cure |
| 8 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2383 A | RTP Company | PUR, Unspecified | RTP |
| Wanthane® WHT-8254 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | Wanthane® |
| ADDILENE J 380 | ADDIPLAST | PP Copolymer | ADDILENE |
| Generic TPC-ET | Generic | TPC-ET | Generic |
| Glasrod SG-200 | Glastic Corporation | Polyester, TS | Glasrod |