Braskem PE HF2207B5
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nAQvxv_Braskem-PE-HF2207B5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The HF2207B5 resin is a linear low density polyethylene, hexene copolymer, produced through Unipol® process and recommended for blown film extrusion. Have high impact and puncture resistance, high coefficient of friction (COF) and high weld rupture resistance. Application: Heavy duty bags, liners, lamination and high COF films. Additive:
Process: Blown film e extrusion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.73 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Break, 20 µm | 47.0 | MPa | ASTM D882 |
| TD : Break, 20 µm | 35.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 990 | % | ASTM D882 |
| TD : Break, 20 µm | 1300 | % | ASTM D882 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD : 20 µm | 150 | MPa | ASTM D790 |
| 1% Secant, TD : 20 µm | 170 | MPa | ASTM D790 |
| Dart Drop Impact 1(20 µm) | 140 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 110 | g | ASTM D1922 |
| TD : 20 µm | 250 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm) | 50 | ASTM D2457 | |
| Haze | 14 | % | ASTM D1003 |
| Injection instructions |
|---|
| Recommended Blow Film Conditions: Temperature Profile: 180°C to 210°C Melt Temperature: < 215°C Blow-up Ratio: 1.8:1 to 2.5:1 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 502-A Phillips Process | Marco Polo International, Inc. | HDPE | MARPOL® |
| Dialon 507 | DTR S.r.l. (Develop Thermoplastic Resins) | PC | Dialon |
| EPIMIX PBT GV0 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | PBT | EPIMIX |
| ESTADIENE 3510 HT | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Lupolen UHM 5000 | LyondellBasell Industries | UHMWPE | Lupolen |