Lumid® GN1001BF
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n9m7Xs_Lumid-GN1001BF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Halogen Free Flame Retardant Applications Connectors |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C, 3.20 mm) | 0.90 - 1.6 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 78.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 18 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 3330 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 113 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 230 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 85.0 | °C | ASTM D648 |
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 3.00 | ASTM D150 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 to 0.820mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 255 - 270 | °C | |
| Middle Temperature | 260 - 275 | °C | |
| Front Temperature | 260 - 275 | °C | |
| Nozzle Temperature | 270 - 280 | °C | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Back Pressure 5 | 0.490 - 1.96 | MPa | |
| Screw Speed | 60 - 200 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.01% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Hydraulic Type |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SEP-600X40 | SHIN-A T&C | Phenolic | SHIN-A |
| TEKNIFLEX® VPOA12200 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/EVOH/PE/PCTFE | TEKNIFLEX® |
| TUFNYL® RXXIC NATURAL | SRF Ltd. | Nylon 66 | TUFNYL® |
| Integra™ PC 5025 NX UV BK4001 | PolySource, LLC | PC | Integra™ PC |
| LNP™ VERTON™ RVL36SXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ VERTON™ |