Celstran® PA66-GF50-0112P7,5/10
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n9ZyiK_Celstran-PA66-GF50-0112P7-5-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Material code according to ISO 1043-1: PA66 Nylon 66/6 Copolymer reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 7.5 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 16400 | MPa | ISO 527-2/1A/1 |
| 80°C | 10000 | MPa | ISO 527-2/1A |
| Tensile Stress | |||
| Fracture | 220 | MPa | ISO 527-2/1A/5 |
| 80°C | 140 | MPa | ISO 527-2/1A |
| Tensile Strain | |||
| Fracture | 1.6 | % | ISO 527-2/1A/5 |
| Fracture, 80°C | 2.4 | % | ISO 527-2/1A |
| Flexural Modulus (23°C) | 14000 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 300 | MPa | ISO 178 |
| 80°C | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 36 | kJ/m² | ISO 179/1eA |
| 23°C | 35 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 59 | kJ/m² | ISO 179/1eU |
| 23°C | 61 | kJ/m² | ISO 179/1eU |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 48 | kJ/m² | ISO 180/1U |
| 23°C | 57 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 235 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 220 | °C | ISO 75-2/C |
| Melting Temperature 1 | 240 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 280 - 285 | °C | |
| Middle Temperature | 280 - 290 | °C | |
| Front Temperature | 290 - 300 | °C | |
| Nozzle Temperature | 310 - 320 | °C | |
| Processing (Melt) Temp | 310 - 320 | °C | |
| Mold Temperature | 90.0 - 120 | °C | |
| Injection Pressure | 120 - 150 | MPa | |
| Injection Rate | Moderate | ||
| Holding Pressure | 50.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 300 to 315°CZone 4 Temperature: 300 to 310°CFeed Temperature: 20 to 50°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 30YM240E | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| OCTAL PET MONOLAYER rPET | OCTAL Holding & Co. | PET | OCTAL PET |
| Nypol® PA A3 G50 HS NTLA013 NR356 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| EnCom F2 ABS 6030 | EnCom, Inc. | ABS | EnCom |
| K-Prene GHT 45 | Technovinyl Polymers India Ltd. | TPE | K-Prene |