LNP™ THERMOCOMP™ 2C003 compound
| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n8xevV_LNP-THERMOCOMP-2C003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 2C003 is a compound based on ETFE resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound FP-EC-1003 Product reorder name: 2C003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.73 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 11700 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Break | 90.3 | MPa | |
| Break 2 | 90.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break | 4.9 | % | |
| Break 3 | 4.9 | % | |
| Flexural Modulus | ASTM D790 | ||
| 50.0 mm Span 4 | 11000 | MPa | |
| -- | 11000 | MPa | |
| Flexural Strength | ASTM D790 | ||
| -- | 138 | MPa | |
| Break, 50.0 mm Span 5 | 138 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 350 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1200 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 208 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 300 to 325 | °C | |
| Front Temperature | 325 to 340 | °C | |
| Processing (Melt) Temp | 315 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-6060HT | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Dynacom SLP-20S | Dynachem Co. Ltd. | PP Copolymer | Dynacom |
| Hylon® N2033HL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Karina WHITE PVC COMPOUND -E 836-10/176-CRA | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina NATURAL PVC COMPOUND 900-25/1-C-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |