Radilon® S 40 EPT2808 333 NER
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n8rSa0_Radilon-S-40-EPT2808-333-NER.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA6 high viscosity extrusion grade. Low modulus, high flexibility and high impact strength, even at low temperatures. Black colour. This material has been designed for extrusion of pipes. Typical application: convoluted fuel pipes for the automotive industry. ISO 1043 : PA6-HIP |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.08 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 900 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 35.0 | -- | MPa | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 100 | -- | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 550 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 25.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 65 | -- | kJ/m² | ISO 179/1eA |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 50.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 120 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 220 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 30 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Melt Temperature | 240 to 270 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sofprene T® 550100A50 | SO.F.TER. SPA | SBS | Sofprene T® |
| EVICOM™ GH1/119 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| INEOS PP N00G-01 | INEOS Olefins & Polymers USA | PP Impact Copolymer | INEOS PP |
| LNP™ LUBRICOMP™ RFN16 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |
| ISOTHANE® 3065A-FR | Great Eastern Resins Industrial Co., Ltd. (GRECO) | TPU-Polyether | ISOTHANE® |