RTP 1883A
| Category: | PC+Acrylic , Polycarbonate + Acrylic (PMMA) |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n8Mq3U_RTP-1883A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 5.0E-3 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.18 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11700 | MPa | ASTM D638 |
| Tensile Strength | 114 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 10000 | MPa | ASTM D790 |
| Flexural Strength | 155 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 370 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 132 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as UL 94, was tested in accordance with RTP Company Testing.Molding Shrinkage, ASTM D955, .25in thick: .001 in/in |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 - 271 | °C | |
| Middle Temperature | 232 - 271 | °C | |
| Front Temperature | 232 - 271 | °C | |
| Mold Temperature | 65.6 - 104 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VTM® 264FRB | Cytec Industries Inc. | Epoxy | VTM® |
| Amilan® EA1R21G33 | Toray Resin Company | Nylon 6 | Amilan® |
| Lupol® TE5107 | LG Chem Ltd. | TPO | Lupol® |
| Petrothene® GA643000 | LyondellBasell Industries | LLDPE | Petrothene® |
| SUMIMAC® ECR-9125K | SBHPP | Epoxy | SUMIMAC® |