DESLON™ 66 DSC201HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLON™ 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n88HWX_DESLON-66-DSC201HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLON™ DSC201HS is one of the brands which made by Polyamide66 and unreinforced goods. It provides long term of thermal property, good lubrication, good fluidity property and good injection molding property. Applications: DESLON™ DSC201HS is one of the most-used for long term of thermal property and mechanical property goods, such as automotive parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.8 - 2.0 | % | |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 82.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 2940 | MPa | ASTM D790 |
| Flexural Strength | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 230 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 85.0 | °C | ASTM D648 |
| Melting Temperature | 260 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 23 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.20 | ASTM D150 | |
| Arc Resistance | 190 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 285 | °C | |
| Front Temperature | 285 - 290 | °C | |
| Nozzle Temperature | 280 - 285 | °C | |
| Processing (Melt) Temp | 280 - 285 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID B 280 G3 X0 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Adell PP RP-14 | Adell Plastics, Inc. | PP Copolymer | Adell PP |
| Aristech Acrysteel® IGP | Aristech Acrylics LLC | Acrylic, Unspecified | Aristech |
| EPLAMID 6 CBR 30 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| Kynar® MG15 | Arkema | PVDF | Kynar® |