Hifax 5519/1
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n83aQK_Hifax-5519-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hifax" 5519/1 is a PP/EPR-Blend, mineral filled, impact modified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 2554 | ||
| Across Flow | 1.1 | % | |
| Flow | 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 17.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 100 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | |
| -20°C | 8.0 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ISO 306/A50 |
| CLTE - Flow 2(30 to 85°C) | 7.0E-5 | cm/cm/°C | DIN 53752 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | Final Part |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Torelina® A305MD1 | Toray Resin Company | PPS | Torelina® |
| Vydyne® R525H BLK | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Axiall PVC CL-6380J | Axiall Corporation | PVC, Rigid | Axiall PVC |
| LUVOCOM® 1-9051/LGF/BK | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Deprene 201-73 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |