| Standard injection moulding grade for thin-walled parts |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 8.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.8 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(23°C) | 3150 | 1600 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Yield, 23°C) | 83.0 | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain 3(Yield, 23°C) | 4.5 | 21 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break 4(23°C) | 15 | > 50 | % | ISO 527-2/50 |
| Flexural Stress 5(23°C) | 135 | 65.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 6 | ISO 179/1eA | |||
| -30°C | 4.0 | 6.0 | kJ/m² | |
| 23°C | 6.0 | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength 7 | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength 8 | ISO 180/1A | |||
| -30°C | 3.0 | 3.0 | kJ/m² | |
| 23°C | 5.0 | 11 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 9 | ||||
| 0.45 MPa, Unannealed | 190 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 10 | 262 | -- | °C | ISO 3146 |
| CLTE - Flow 11(4.00 mm) | 8.5E-5 | -- | cm/cm/°C | DIN 53752 |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 90 | -- | °C | |
| some hours | 200 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 12 | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity 13 | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength 14 | 32 | 26 | kV/mm | IEC 60243-1 |
| Relative Permittivity 15(1 MHz) | 3.60 | 5.00 | IEC 60250 | |
| Dissipation Factor 16(1 MHz) | 0.025 | 0.20 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 17 | V-2 | -- | ||
| 1.60 mm 18 | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | Test Specimen accordng to ISO 3167, Type A |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 80x10x4 mm |
| 8 . | 80x10x4 mm |
| 9 . | 110x10x4mm |
| 10 . | 10 K/min, Compound for moulding |
| 11 . | >=10x10x4 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 80x80x1 mm |
| 15 . | 80x80x1 mm |
| 16 . | 80x80x1 mm |
| 17 . | 125x13x0.8 mm |
| 18 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800 64A | RTP Company | TPO (POE) | RTP |
| SLOVASTER® B1 GF 20 000/2 | Plastcom | PBT | SLOVASTER® |
| Styropor® F 295 E | BASF Corporation | PS (EPS) | Styropor® |
| Electrafil® PA6 C BK | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| LUVOCOM® 50-8479/BL-1 | Lehmann & Voss & Co. | PC | LUVOCOM® |