SABIC® LDPE 2022TN00
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n6rGHs_SABIC-LDPE-2022TN00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2022TN00 is specially developed for applications that require a good balance between flow properties and mechanical properties, e.g. toys, household articles, clamping lids. SABIC® LDPE 2022TN00 is not suitable for food applications. The alternative for food applications is SABIC® LDPE 1922T. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 22 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 75 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 29.0 | cm³/10min | ISO 1133 |
| 190°C/5.0 kg | 98.0 | cm³/10min | ISO 1133 |
| Environmental Stress-Cracking Resistance 1(60°C, 3.00 mm, Rhodacal-DS10, Compression Molded) | 3.00 | hr | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C, Molded) | 45 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 175 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 23°C, 2.00mm, molded | 8.00 | MPa | ISO 527-2/1BA/50 |
| Fracture, 23°C, 2.00mm, molded | 7.00 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | 400 | % | ISO 527-2/1BA/50 |
| Tensile Creep Modulus 2 | ISO 899-1 | ||
| 1 hr | 80.0 | MPa | ISO 899-1 |
| 1000 hr | 45.0 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/A | ||
| -30°C, molded | 5.0 | kJ/m² | ISO 180/A |
| 23°C, molded | 42 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 39.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 82.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 105 | °C | DIN 53765 |
| Enthalpy Change | 104 | J/g | DIN 53765 |
| Note Message | |
|---|---|
| 1 . | 2 MPa |
| 2 . | thickness 4 mm, determined at 23 °C, 3 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 Z | RTP Company | ABS | RTP |
| Sup-tech C9000 | Shanghai Suptech Engineering Plastics Co. Ltd. | PC | Sup-tech |
| Tuftec™ P1500 | AKelastomers | SBBS | Tuftec™ |
| INSTRUC PCGF30 | Infinity LTL Engineered Compounds | PC | INSTRUC |
| INSULCAST® 116 FR | ITW Polymers Coatings North America | Epoxy | INSULCAST® |