Talcoprene® 1540TL1 NERO
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Talcoprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n5AKzF_Talcoprene-1540TL1-NERO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer, 40% mineral filled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 1.0 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Ash Content | 40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 28.0 | MPa | ASTM D638 |
| Flexural Modulus | 3900 | MPa | ASTM D790 |
| Flexural Strength | 50.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 26 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 71.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 1 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Dielectric Constant (1 kHz) | 2.50 | ASTM D150 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 190 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 230 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-6830 | Sumitomo Bakelite Co., Ltd. | Phenolic | Sumikon® |
| Sypex S1420GN | Ginar Technology Co., LTD. | SAN | Sypex |
| GAPEX® HPP40GR22RD | Ferro Corporation | PP Homopolymer | GAPEX® |
| Isocor™ 4007 | Shakespeare Monofilaments and Specialty Polymers | Nylon 6 | Isocor™ |
| LG ASA LI923P | LG Chem Ltd. | ASA | LG ASA |