Vipel® K022-CDC-00

Category: Vinyl Ester , Vinyl Ester
Manufacturer: AOC, L.L.C.
Trademark: Vipel®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: n4bSOt_Vipel-K022-CDC-00.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Vipel Fire Retardant Bisphenol A, Epoxy Vinyl Ester Resin

AOC's Vipel K022 series is a brominated bisphenol A epoxy vinyl ester resin dissolved in styrene. Vipel K022 series is ideally suited for use in hand lay-up, spray-up, filament winding and pultrusion processes where outstanding mechanical properties and excellent resistance to chemicals and heat are required. Vipel K022-CN series contains antimony products.

Fire Retardant
Some Vipel K022 versions do not require antimony trioxide to meet ASTM E 84 Class I flame spread requirements.

Mechanical Properties
Vipel K022 is suitable for moldings that are subjected to particularly high static or dynamic loads. Vinyl ester resins have excellent resistance to sustained heat.

Versatile
Wide formulating capabilities allow for use in many processes and for optimization of cost/performance.

Corrosion Resistance
Vipel K022 is highly resistant to a number of chemical environments. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC.
General Information
Additive
  • Flame Retardant
Features
  • Brominated
  • Flame Retardant
  • Good Chemical Resistance
  • Good Corrosion Resistance
  • High Heat Resistance
Uses
  • Coating Applications
  • Filaments
Forms
  • Liquid
Processing Method
  • Filament Winding
  • Hand Lay-up
  • Pultrusion
  • Spraying
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.13g/cm³ASTM D792
Bound Styrene 42.0%
HardnessNominal ValueUnitTest Method
Barcol Hardness 40ASTM D2583
MechanicalNominal ValueUnitTest Method
Tensile Modulus ASTM D638
    25°C, Cast 3600MPa
    66°C, Cast 3000MPa
    93°C, Cast 2800MPa
    121°C, Cast 900MPa
    135°C, Cast 10.0MPa
Tensile Strength ASTM D638
    25°C, Cast 83.0MPa
    66°C, Cast 68.0MPa
    93°C, Cast 50.0MPa
    121°C, Cast 8.00MPa
    135°C, Cast 1.50MPa
Tensile Elongation ASTM D638
    Break, 25°C, Cast 4.6%
    Break, 66°C, Cast 5.1%
    Break, 93°C, Cast 6.1%
    Break, 121°C, Cast > 10%
    Break, 135°C, Cast 12%
Flexural Modulus (25°C, Cast)3700MPaASTM D790
Flexural Strength (25°C, Cast)143MPaASTM D790
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, Cast)112°CASTM D648
FlammabilityNominal ValueTest Method
Flame Spread 10.0ASTM E84
Smoke Developed 800ASTM E84
ThermosetNominal ValueUnitTest Method
Gel Time 1(25°C)22.0min
Additional InformationNominal ValueUnitTest Method
Antimony Trioxide 1.50ISO 6383-2
Gel to Peak 12.0min
Peak Exotherm 168°C
ThermosetNominal ValueUnitTest Method
Shelf Life 26wk
Thermoset Mix Viscosity 2(25°C)350cPASTM D2393
Note Message
1 .with 0.3% Cobalt 6%, 0.05 % DMA and 1.25% MEKP
2 .Brookfield RV viscosity spindle 2 at 20 rpm
Resin Grade Manufacturer Category Trademark
Zytel® RS LC3090 NC010 DuPont Performance Polymers Nylon 610 Zytel® RS
ENFLEX V1073A BLK UV ENPLAST Americas, a Ravago Group Company TPV ENFLEX
Hyundai EP Matt MF503/Natural HYUNDAI EP Co., Ltd. Polyolefin, Unspecified Hyundai EP Matt
SECCO S1003 Shanghai SECCO Petrochemical Co., Ltd PP Homopolymer SECCO
Elastoprene HS5150D NAT KMI Group, Inc. TPO (POE) Elastoprene