LUVOTECH® GS 46 Datasheet,Nylon 46,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOTECH®GS 46 is a polyamide 46 (nylon 46) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOTECH®The main features of GS 46 are: Good dimensional stability heat stabilizer Lubrication Typical application areas include: textile/fiber engineering/industrial accessories Automotive Industry business/office supplies

General Information
Additive	heat stabilizer Lubricant
Features	Good dimensional stability Thermal Stability Lubrication
Uses	Textile applications Engineering accessories Application in Automobile Field Business equipment
Appearance	Grey

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Molding Shrinkage	1.0 - 1.5	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 1.5	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3900	MPa	ISO 527-2
Tensile Stress (Break)	100	MPa	ISO 527-2
Tensile Strain (Yield)	5.0	%	ISO 527-2
Coefficient of Friction
Dynamic	0.31
Static	0.23

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	12	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	90	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	160	°C	ISO 75-2/A
Continuous Use Temperature	150	°C	UL 746B
Maximum operating temperature- Short Term	160	°C
Vicat Softening Temperature	280	°C	ISO 306/A

Injection	Nominal Value	Unit
Drying Temperature
A	80.0	°C
Vacuum dryer, B	80.0	°C
Drying Time
A	2.0 - 8.0	hr
Vacuum dryer, B	2.0 - 12	hr
Suggested Max Moisture	0.10	%
Rear Temperature	285 - 315	°C
Middle Temperature	305 - 315	°C
Front Temperature	305 - 315	°C
Nozzle Temperature	280 - 330	°C
Processing (Melt) Temp	310	°C
Mold Temperature	120 - 140	°C

Injection instructions
General In general LUVOTECH® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOTECH® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 46 , Polyamide 46
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOTECH®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	n3QSXH_LUVOTECH-GS-46.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Starflam PF0057E	Eurostar Engineering Plastics	Nylon 6	Starflam
CERTENE™ LDI-5523	Muehlstein	LDPE	CERTENE™
Fainplast PVC PKS 78	Fainplast Compounds S.r.l	PVC, Flexible	Fainplast PVC
Ketjenflex® 8	Axcentive SARL	Plasticizer	Ketjenflex®
Hyundai EP TPO HR525	HYUNDAI EP Co., Ltd.	TPO (POE)	Hyundai EP TPO