Badamid® B70 SM-Z3
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n3Csir_Badamid-B70-SM-Z3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid®B70 SM-Z3 is a polyamide 6 (nylon 6) material,. This product is available in Europe,. Badamid®The main characteristics of B70 SM-Z3 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.08 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.6 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 65.0 | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.5 | 35 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 35 | 50 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, not annealed | 170 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 222 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | 100 | 60 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.60 | 6.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.029 | 0.30 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Short-Term Heat Resistance, IEC 216, 20000 hrs: 170°CLong-Term Heat Resistance, IEC 216, 50% decrease of yield stress: 70°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 110x10x4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F7870 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| QAMAR FD21HS | SPDC Ltd. | LLDPE | QAMAR |
| CALSIN 110FRF | Pooya Polymer Tehran | Polyolefin, Unspecified | CALSIN |
| ESPOLEX WT525 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| Karina BROWN COLOR CONCENTRATE 36/59-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |