PELPRENE™ S3001
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | PELPRENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n2YBzx_PELPRENE-S3001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PELPRENE™S3001 is a thermoplastic polyester elastomer (TPEE) product,. It is available in North America. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.5 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 65% RH) | 0.34 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 540 | % | ASTM D638 |
| Flexural Modulus | 274 | MPa | ASTM D790 |
| Compressive Modulus | 21.1 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles) | 10.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (50% Strain) | 19.6 | MPa | ASTM D412 |
| Tear Strength | 167 | kN/m | ASTM D624 |
| Compression Set | 62 | % | ASTM D395 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 117 | °C | ASTM D648 |
| Brittleness Temperature | -65.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 193 | °C | ASTM D1525 |
| Melting Temperature | 216 | °C | DSC |
| CLTE - Flow | 1.4E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Hardness, JIS k6301, A scale: 9810% Compression Modulus, ASTM D695: 21.1 MPaResilience, JIS K6301: 58 %Brittle Point, JIS K6301: < -65 °CCompression Set, JIS K6301: 62 %Coefficient of Linear Thermal Expansion, TMA: 14e-5 1/K |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 A TFE 15 SI 2 | RTP Company | PPA | RTP |
| Clariant Nylon 6/6 6601-L BK-09 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Karina MBU BLUE -E 06/948-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ PF008S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| ADREF® O05NOEGD01V2 | A.D. Compound S.p.A. | PP Copolymer | ADREF® |