Ultramid® B3ZG3
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n2M5lN_Ultramid-B3ZG3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3ZG3 is an impact-modified, 15% glass fiber reinforced injection molding PA6 grade. Applications Typical applications include automobile cable conduits. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.22 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 35.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | -- | % | |
| Water Absorption | ||||
| Saturation | 7.5 | -- | % | ASTM D570 |
| Saturation, 23°C | 7.5 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.4 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 5500 | 2900 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Break, 23°C | 103 | -- | MPa | ASTM D638 |
| Break, 23°C | 110 | 60.0 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, 23°C | 4.0 | -- | % | ASTM D638 |
| Break, 23°C | 4.0 | 18 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 4480 | -- | MPa | ASTM D790 |
| 23°C | 4500 | 2500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 150 | 80.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 7.0 | -- | kJ/m² | |
| 23°C | 16 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 55 | -- | kJ/m² | |
| 23°C | 75 | 110 | kJ/m² | |
| Notched Izod Impact | ||||
| -40°C | 53 | -- | J/m | ASTM D256 |
| 23°C | 110 | -- | J/m | ASTM D256 |
| 23°C | 15 | 29 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 204 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 193 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 180 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE | ||||
| Flow | 3.3E-5 | -- | cm/cm/°C | |
| Transverse | 7.5E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.730 mm | 150 | -- | °C | |
| 1.50 mm | 150 | -- | °C | |
| 3.00 mm | 150 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.730 mm | 115 | -- | °C | |
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.730 mm | 150 | -- | °C | |
| 1.50 mm | 150 | -- | °C | |
| 3.00 mm | 150 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | 1.0E+13 | 1.0E+10 | ohms·cm | ASTM D257 |
| -- | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.70 | 6.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.025 | 0.20 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.730 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 245 to 275 | °C | |
| Middle Temperature | 260 to 285 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badaflex® TPE-S 45A 1000LD | Bada AG | TPE | Badaflex® |
| Baoding 67I80 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Altuglas® BS 150N | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| ExxonMobil™ LLDPE LL 6101 Series | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| ALTECH® PP-H A 1000/578 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |