INSTRUC PPSBGF30
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INSTRUC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n1DgC6_INSTRUC-PPSBGF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS FIBER REINFORCED BRANCHED POLYPHENYLENE SULFIDE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 0.20 to 0.40 | % | |
| Across Flow : 3.18 mm | 0.40 to 0.70 | % | |
| Water Absorption (Equilibrium) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13100 | MPa | ASTM D638 |
| Tensile Strength (Break) | 131 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 321 to 332 | °C | |
| Mold Temperature | 135 to 177 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 7.6E-3 to 0.013 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S RCP3010LK 333 NER | Radici Plastics | Nylon 6 | Radilon® |
| Moplen RP241G | LyondellBasell Industries | PP Random Copolymer | Moplen |
| AKROMID® A3 GF 50 natural (2423) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| EPO-TEK® TV1003-LV | Epoxy Technology Inc. | PI, TS | EPO-TEK® |
| Iupilon® H-3000 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |