Iupital® TC3030
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n0fmSU_Iupital-TC3030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Iupital® TC3030 is an Acetal (POM) Copolymer material filled with 30% talc. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Iupital® TC3030: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 6.90 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.00 mm) | 1.5 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 62.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ISO 178 |
| Flexural Stress | 111 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 144 | °C | ISO 75-2/A |
| Melting Temperature | 166 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 170 | °C | |
| Middle Temperature | 180 | °C | |
| Front Temperature | 190 | °C | |
| Nozzle Temperature | 180 to 210 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 50.0 to 100 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 80 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V150-72A | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Next Nylon 66 Prime Series PMTHS-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| EPO-TEK® OE101 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Microthene® MP652762 | LyondellBasell Industries | HDPE | Microthene® |
| Petrothene® FR200000 | LyondellBasell Industries | Polyolefin, Unspecified | Petrothene® |