Nivionplast® B C306MB NERO900
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Nivionplast® B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n0RYTX_Nivionplast-B-C306MB-NERO900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nivionplast® B C306MB NERO900 is a Polyamide 6 (Nylon 6) material. It is available in Europe, Latin America, or North America for injection molding. Important attributes of Nivionplast® B C306MB NERO900 are:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 1.1 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 7.0 | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | % | |
| Ash Content | 30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4900 | MPa | ASTM D638 |
| Tensile Strength (Break) | 87.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.3 | % | ASTM D638 |
| Flexural Modulus | 4700 | MPa | ASTM D790 |
| Flexural Strength | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 200 | °C | |
| 1.8 MPa, Unannealed | 75.0 | °C | |
| Peak Melting Temperature | 220 | °C | ASTM D3417 |
| CLTE - Flow | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 250 | °C | |
| Middle Temperature | 270 | °C | |
| Front Temperature | 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 MR 209 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| WPP PP PPH2CF2P-White | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Hostacom TRC 452N | LyondellBasell Industries | PP Copolymer | Hostacom |
| Lupolen 3020 F | LyondellBasell Industries | LDPE | Lupolen |
| Sylvin 916VO Grey 9371 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |