Generic TSU
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mzym1O_Generic-TSU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TSU This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.999 to 1.26 | g/cm³ | ASTM D792 |
| -- | 1.02 to 1.15 | g/cm³ | ASTM D1505 |
| Apparent Density | 1.01 to 1.09 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (23°C) | 0.060 to 0.42 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 14 to 96 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 0.186 to 285 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 2.35 to 44.3 | MPa | |
| 23°C | 0.379 to 69.4 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 10 to 810 | % | |
| Break, 23°C | 8.5 to 800 | % | |
| Flexural Modulus (23°C) | 24.8 to 4470 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 6.69 to 115 | MPa | ASTM D790 |
| Coefficient of Friction | 0.79 to 0.80 | ASTM D1894 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain, 23°C | 0.290 to 9.12 | MPa | |
| 200% Strain, 23°C | 1.24 to 17.2 | MPa | |
| 300% Strain, 23°C | 0.414 to 13.0 | MPa | |
| Tensile Strength | ASTM D412 | ||
| Yield, 23°C | 2.38 to 26.5 | MPa | |
| Break, 23°C | 1.62 to 38.4 | MPa | |
| Tensile Elongation (Break, 23°C) | 2.0 to 810 | % | ASTM D412 |
| Tear Strength | |||
| 23°C | 4.20 to 69.7 | kN/m | ASTM D624 |
| Split | 27 | kN/m | ASTM D470 |
| Compression Set | 2.7 to 72 | % | ASTM D395 |
| Bayshore Resilience | 47 to 59 | % | ASTM D2632 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 14 to 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 53.1 to 117 | °C | |
| 1.8 MPa, Unannealed | 46.0 to 96.0 | °C | |
| Brittleness Temperature | -67.8 to -66.8 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.9E+10 to 7.1E+16 | ohms | ASTM D257 |
| Dielectric Constant (23°C) | 3.54 to 6.61 | ASTM D150 | |
| Dissipation Factor (23°C) | 0.010 to 0.10 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 7.4 to 45 | min | |
| Shelf Life (23°C) | 24 to 78 | wk | |
| Thermoset Mix Viscosity | 10.0 to 3720 | cP | ASTM D2393 |
| Demold Time | 5.0 to 440 | min | |
| Post Cure Time | 3.0 to 150 | hr |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity (23°C) | 0.040 to 1.2 | Pa·s | |
| Curing Time (23°C) | 24 to 1.7E+2 | hr | |
| Gel Time (23°C) | 0.50 to 27 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (23°C) | 50 to 90 | ||
| Tensile Modulus (23°C) | 1030 to 1860 | MPa | |
| Tensile Strength (23°C) | 1.14 to 69.3 | MPa | |
| Tensile Elongation at Break (23°C) | 2.0 to 100 | % | |
| Tear Strength (23°C) | 3.50 to 30.8 | kN/m |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP TIVAR® 88 BurnGuard | Quadrant Engineering Plastic Products | UHMWPE | Quadrant EPP |
| SCANAMID 6 B12^ NH11L | Polykemi AB | Nylon 6 | SCANAMID 6 |
| Fainplast PVC CTS 01426/1 | Fainplast Compounds S.r.l | PVC Alloy | Fainplast PVC |
| ECOZEN® T95 | SK Chemicals | Copolyester, Bio-based | ECOZEN® |
| Epic Epoxy S7397-01 | Epic Resins | Epoxy | Epic Epoxy |