NORYL™ NH6010B resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mzqaiQ_NORYLNH6010Bresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity. This grade can be processed via extrusion or injection molding. NORYL NH6010B is available in custom colors and may be an excellent material candidate for use in building and construction and electrical markets. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 5.7 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 5.70 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2220 | MPa | ASTM D638 |
| -- | 2440 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 64.0 | MPa | ASTM D638 |
| Yield | 64.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 53.0 | MPa | ASTM D638 |
| Fracture | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.6 | % | ASTM D638 |
| Yield | 4.7 | % | ISO 527-2/50 |
| Fracture 5 | 20 | % | ASTM D638 |
| Fracture | 8.3 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2390 | MPa | ASTM D790 |
| -- 7 | 2360 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 180 | J/m | ASTM D256 |
| 23°C | 300 | J/m | ASTM D256 |
| -30°C 10 | 15 | kJ/m² | ISO 180/1A |
| 23°C 11 | 19 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 52.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 122 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 124 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 146 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.3E+18 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 7.6E+17 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | |||
| 3.20 mm, in Oil | 34 | kV/mm | ASTM D149 |
| 3.20mm, in oil | 34 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 2.78 | ASTM D150, IEC 60250 | |
| Dissipation Factor (1 MHz) | 2.9E-3 | ASTM D150, IEC 60250 | |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.50 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | IEC 60695-2-13 |
| 2.00 mm | 775 | °C | IEC 60695-2-13 |
| 3.00 mm | 800 | °C | IEC 60695-2-13 |
| Oxygen Index | 34 | % | ISO 4589-2 |
| Ds_4min | 70 | ISO 5659-2 | |
| F1 Class Smoke and Toxicity Rating | 3.00 | mm | NF F16-101 |
| Flame Spread Index (1.52 mm) | 15.0 | ASTM E162 | |
| Heat Release, MAHRE | 33.6 | kW/m² | ISO 5660-1 |
| Lateral Flame Spread, CFE | 20.0 | kW/m² | ISO 5658-2 |
| M1 Flame Class Rating | 2.00 | mm | NF P 92501 |
| NBS Smoke Density | ASTM E662 | ||
| Flaming, 20 min : 3.20 mm | 120 | ASTM E662 | |
| Flaming, 4 min : 1.52 mm | 30.0 | ASTM E662 | |
| Flaming, 4 min : 3.20 mm | 30.0 | ASTM E662 | |
| Non-Flaming, 4 min : 1.52 mm | 7.00 | ASTM E662 | |
| Toxicity | |||
| -- | 0.0200 | ISO 5659-2 | |
| 3.00 mm | 21.8 | NF X70-100 |
| Extrusion instructions |
|---|
| Profile Extrusion Parameters: Adapter Temperature: 220 - 260 °C Barrel - Zone 1 Temperature: 220 - 260 °C Barrel - Zone 2 Temperature: 220 - 260 °C Barrel - Zone 3 Temperature: 220 - 260 °C Barrel - Zone 4 Temperature: 220 - 260 °C Calibrator Temperature: 30 - 60 °C Die Temperature: 220 - 260 °C Drying Temperature: 95 - 105 °C Drying Time: 2 - 4 hrs Drying Time (Cumulative): 12 hrs Hopper Temperature: 80 - 120 °C Maximum Moisture Content: 0.07 % Melt Temperature: 220 - 260 °C Water Bath Temperature: 30 - 50 °C Sheet Extrusion Parameters: Adapter Temperature: 220 - 260 °C Barrel - Zone 1 Temperature: 220 - 260 °C Barrel - Zone 2 Temperature: 220 - 260 °C Barrel - Zone 3 Temperature: 220 - 260 °C Barrel - Zone 4 Temperature: 220 - 260 °C Die Temperature: 220 - 260 °C Drying Temperature: 95 - 105 °C Drying Time: 2 - 4 hrs Drying Time (Cumulative): 12 hrs Maximum Moisture Content: 0.07 % Melt Temperature: 220 - 260 °C Roll Stack Temp - Bottom: 90 - 150 °C Roll Stack Temp - Middle: 90 - 150 °C Roll Stack Temp - Top: 90 - 150 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Star L PA66 30V D31 | Eurostar Engineering Plastics | Nylon 66 | Star L |
| VINIKA® T620 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| Cogegum® GFR/350 | Solvay Specialty Polymers | Polyolefin, Unspecified | Cogegum® |
| Fainplast PVC GS 62/T | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Formolene® 6550A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |