PENTAMID A S MK30 H FR natural
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mzX5Wm_PENTAMIDASMK30HFRnatural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low viscosity, heat stabilised polyamide 66, 30% mineral filled, flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.5 | % | ISO 294-4 |
| Flow | 1.5 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 4.9 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.6 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 110 | °C | ISO 75-2/A |
| Melting Temperature | 260 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating (0.8 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (0.8 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.8 mm) | 825 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA66, MFHR, 12-070, MD30 (FR) | ISO 1874 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.13 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 275 - 300 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 78.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 126F9 | SAX Polymers | Nylon 6 | SAXAMID™ |
| DuraSurf™ Galleria | Crown Plastics | UHMWPE | DuraSurf™ |
| Generic PBT - Glass Bead\Glass Fiber | Generic | PBT | Generic |
| Iupiace® AN70 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Karina CRYSTAL CLEAR PVC COMPOUND -E 80/224-IS-SD-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |