ALAMID® 6.6 GK 50

Category: Nylon 66 , Polyamide 66
Manufacturer: LEIS Polytechnik - polymere Werkstoffe GmbH
Trademark: ALAMID®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: myyLvd_ALAMID-6-6-GK-50.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
polyamide 6.6 + 50% glass beads
General Information
Filler / Reinforcement
  • Glass Bead, 50% Filler by Weight
PhysicalNominal ValueUnitTest Method
Density 1.50g/cm³ISO 1183
Viscosity Number (H2SO4 (Sulphuric Acid))140cm³/gISO 307
MechanicalNominal ValueUnitTest Method
Tensile Modulus 5800MPaISO 527-2
Tensile Stress (Yield)85.0MPaISO 527-2
Tensile Strain (Yield)7.0%ISO 527-2
ImpactNominal ValueUnitTest Method
Charpy Notched Impact Strength 2.0kJ/m²ISO 179/1eA
Charpy Unnotched Impact Strength 20kJ/m²ISO 179/1eU
ThermalNominal ValueUnitTest Method
Heat Deflection Temperature (0.45 MPa, Unannealed)225°CISO 75-2/B
Melting Temperature (DSC) 1260°CISO 3146
ElectricalNominal ValueUnitTest Method
Comparative Tracking Index (Solution A)450VIEC 60112
FlammabilityNominal ValueUnitTest Method
Flame Rating (3.20 mm)HBUL 94
Glow Wire Flammability Index (2.00 mm)650°CIEC 60695-2-12
Note Message
1 .10K/min
Resin Grade Manufacturer Category Trademark
Mirakutoran® TPU P890 Japan Mirakutoran Inc. TPU Alloy Mirakutoran® TPU
NANCAR® 1042 Nantex Industry Co., Ltd. NBR NANCAR®
Borealis PE CC8207 Borealis AG LDPE Borealis PE
LNP™ STAT-KON™ KX02764 compound SABIC Innovative Plastics Acetal (POM) Copolymer LNP™ STAT-KON™
LUVOCOM® 1-8843 Lehmann & Voss & Co. Nylon 66 LUVOCOM®