BJB Polyurethane WC-788 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mypXsB_BJB-Polyurethane-WC-788-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WC-788 A/B is an impact resistant, rigid, 84 Shore D aliphatic polyurethane that is commonly used to make clear or tinted castings of all kinds. Note: WC-788 A/B requires post-curing. Thin section casts, less than 1/2" thick, may require in mold post-curing. Product Highlights:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Specific Gravity | |||
| Part A | 1.077 | g/cm³ | |
| Part B | 1.037 | g/cm³ | |
| Shrinkage 1 | 0.60 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Demold Time (25°C) | 16.0 - 24.0 | hr | |
| Work Time (25°C) 2 | 15.0 - 20.0 | min |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Brokfield Viscosity | |||
| Mixed : 25°C | 600 - 700 | mPa·s | |
| Part A : 25°C | 650 | mPa·s | |
| Part B : 25°C | 750 | mPa·s |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure Time (25°C) | 5.0 - 7.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 82 - 86 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1860 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 57.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 20 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 77.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 79.4 | °C | ASTM D648 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Component B | Mixing ratio by weight: 75, mixing ratio by capacity: 78 | ||
| Shelf Life | 26 | wk |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 150-180°F (66-82°C). Support of the part may be required to prevent part deformation during heat cure. |
| Note Message | |
|---|---|
| 1 . | 12"x1/2"x1/2" |
| 2 . | 100g mass - The 15-20 minute work time is the standard in-stock product. Products with 5, 30, 60, 90, 180 and 240 minute work times are available on a special order basis. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yanshan PE 7300M | SINOPEC Beijing Yanshan Petrochemical | HDPE | Yanshan PE |
| ExxonMobil™ PP1013H1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Gallonprene® GP540-8505 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| ESTABLEND 6600 | Cossa Polimeri S.r.l. | ASA+PC | ESTABLEND |
| NORYL™ WCP921 resin | SABIC Innovative Plastics Asia Pacific | PPE+TPE | NORYL™ |