Vydyne® R515H Natural
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | myg4HY_Vydyne-R515H-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vydyne R515H Natural is high-flow, heat-stabilized, hydrolysis-resistant, 15% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is also lubricated for improved flow and offers superior surface appearance. Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep, and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents. Vydyne R515H Natural is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R515H Natural has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions. Typical Applications/End Uses: Vydyne R515H Natural is successfully used in a wide range of injection molding engineering applications, including automotive clips, radiator end tanks, parts of the air-conditioning and petrol distribution system, etc. (under the hood); electrical connectors, housings, bobbins, etc.; and in industrial applications such as gears, bearing shells, covers, housings, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.24 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 1.0 | -- | % | |
| Flow : 23°C, 2.00 mm | 0.50 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6600 | 4000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 120 | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | 13 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5900 | 3250 | MPa | ISO 178 |
| Flexural Stress (23°C) | 170 | 110 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 6.0 | 5.3 | kJ/m² | |
| 23°C | 6.0 | 7.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 32 | 38 | kJ/m² | |
| 23°C | 39 | 43 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 5.7 | 5.4 | kJ/m² | |
| 23°C | 6.6 | 7.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 258 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 241 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 3.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 1.1E-4 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 140 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 120 | -- | °C | |
| 1.50 mm | 120 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 125 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (0.750 mm) | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 20 | -- | kV/mm | IEC 60243 |
| Arc Resistance (3.00 mm) | PLC 6 | -- | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 250 to 399 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.750 mm | PLC 4 | -- | ||
| 1.50 mm | PLC 3 | -- | ||
| 3.00 mm | PLC 4 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.750 mm | 675 | -- | °C | |
| 1.50 mm | 675 | -- | °C | |
| 3.00 mm | 675 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 700 | -- | °C | |
| 1.50 mm | 700 | -- | °C | |
| 3.00 mm | 700 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ M95 | Miracll Chemicals Co., Ltd. | TPU-Polyether | Mirathane™ |
| Styrolution PS 168N | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| Adflex Z 108 S | LyondellBasell Industries | Polyolefin, Unspecified | Adflex |
| APEX® 85-J644-M | Teknor Apex Company | PVC, Flexible | APEX® |
| Idealis 500 | Braskem | HMWPE | Idealis |