ACCUTECH™ HP0336T20L1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | my3GNy_ACCUTECH-HP0336T20L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0336T20L1 is a polypropylene homopolymer (PP Homopoly) product, which contains 20% talc filler. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 36.0 | MPa | ASTM D638 |
| Fracture | 28.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | ASTM D638 |
| Fracture | 16 | % | ASTM D638 |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 49.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 125 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 70.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VNC107E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| NYLOY® M-0030N-V | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| Leona™ 14G33 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Plenco 04311 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |
| StarFlex® 7360-9000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |