| Epiall 1908K-2 is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability and high strength properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.95 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.15 - 0.35 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 70 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 97.0 | MPa | ASTM D638 |
| Flexural Modulus | 18600 | MPa | ASTM D790 |
| Flexural Strength (Break) | 166 | MPa | ASTM D790 |
| Compressive Strength | 240 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 282 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow | 1.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 3.8E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 13 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.017 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Additional Information |
|---|
| Powder Density, ASTM D1895: 0.85 g/cm³Water Absorption, ASTM D570, 48 hrs, 50°C: 0.2%DTUL @264psi - Unannealed, ASTM D648, Post Baked: >282°CDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 12.8 kV/mmDielectric Constant, ASTM D150, 1000000 Hz, wet: 3.8Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.017 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POYAD AS101 | Pooya Polymer Tehran | PP Homopolymer | POYAD |
| ELASTOSIL® R 420/60 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Lanufene LLF 183N | Ras Lanuf Oil & Gas Processing Company (RASCO) | LLDPE | Lanufene |
| Lifoflex® UV 80 GA 1080 | ELASTO | SEBS | Lifoflex® |
| Sylvin 8773-60D Brown 7373 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |