Spartech Polycom SC2-1090U
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mwnGNe_Spartech-Polycom-SC2-1090U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Spartech SC2-1090U is a medium viscosity, high impact polystyrene (HIPS) resin for injection molding that features a UV stabilizer. It is heat stabilized and lubricated for good processing characteristics. HIPS are rubber modified styrenics that typically contain 1-10% rubber by weight. They offer dimensional and physical stability in moist environments and provide good chemical resistance. These materials also exhibit good flexibility along with good toughness. A very versatile product for a wide variety of applications, Spartech SC2-1090U is recommended for industrial, transportation, sporting goods and electrical/electronic applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) | 9.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 22.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 40 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2410 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 43.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 78.5 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 200 - 220 | °C | |
| Middle Temperature | 205 - 225 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Processing (Melt) Temp | 191 - 260 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3400 M-450 | RTP Company | LCP | RTP |
| SCHULADUR® A GB 20 | A. Schulman Europe | PBT | SCHULADUR® |
| Ecodear® V751X52 | Toray Resin Company | PLA | Ecodear® |
| Karina GREEN PVC COMPOUND 950D40/308-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POCAN® DP 7318 000000 | LANXESS GmbH | PBT | POCAN® |