LAMIGAMID® 410
| Category: | Nylon 6 Alloy , Polyamide 6 Alloy |
| Manufacturer: | Schwartz Technical Plastic |
| Trademark: | LAMIGAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | muRyv2_LAMIGAMID-410.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Elastomer modified for temperatures down to -50°C Applications:
|
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Water Absorption (23°C, 24 hr) | 2.3 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 40.0 | MPa | ISO 527-2 |
| Fracture | 20.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 180 | % | ISO 527-2 |
| Flexural Modulus | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 45 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 160 | °C | ISO 75-2/B |
| Melting Temperature (DSC) | 205 | °C | ISO 3146 |
| CLTE - Flow (20 to 100°C) | 1.0E-4 - 1.8E-4 | cm/cm/°C | ISO 11359-2 |
| Additional Information |
|---|
| Safe Temperature Range, permanent: -50° to 60°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR21-1091 | Spartech Polycom | PBT | Spartech |
| Versaflex™ HC MT555 | PolyOne Corporation | TPE | Versaflex™ |
| Borclear™ RE936CF | Borealis AG | PP Random Copolymer | Borclear™ |
| Keltan® 5469 | LANXESS Buna GmbH | EPDM | Keltan® |
| Orevac® T 9318 | Arkema | EVA | Orevac® |