Di-Pak™ E-4501-5
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Di-Pak™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mte4KI_Di-Pak-E-4501-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DI-PAK E-4701, E-4951 and E-4501 Easily pourable, thermally conductive, shock resistant potting compounds that are ideally suited for low and high production applications. This series of DI-PAK products reduce rejects by exhibiting extremely low stress on potted components. All three of the above DI-PAK E products are flame retardant and meet UL 94V-0 requirements. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D2566 |
| Weight - per cubic inch | 24 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Service Temperature | 140 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 5.0 | min | ASTM D2971 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Shock Test | Pass |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 172 | MPa | ASTM D638 |
| Tensile Strength | 14.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 283 | MPa | ASTM D790 |
| Flexural Strength | 18.6 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 78.8 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 2.0E-4 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.40 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 9.6E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | > 16 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 4.50 | ||
| 100 kHz | 4.20 | ||
| Dissipation Factor (25°C, 100 kHz) | 0.055 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 250, Mix Ratio by Volume: 150 | ||
| Thermoset Mix Viscosity (25°C) | 7200 | cP | ASTM D4878 |
| Demold Time (21°C) | 10 to 20 | min |
| Note Message | |
|---|---|
| 1 . | 100 g |
| 2 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultradur® B 2520 | BASF Corporation | PBT | Ultradur® |
| APEX® 04-A769R-60NT | Teknor Apex Company | PVC, Flexible | APEX® |
| DAPCO™ 3021C | Cytec Industries Inc. | Epoxy | DAPCO™ |
| Hipolyene 8501 T6 B | Zylog Plastalloys | TPO (POE) | Hipolyene |
| POROPHEN® GF 9200 L12 | SBHPP | Phenolic | POROPHEN® |